E-Polymers TEKAMID® TA210ST Super Tough PA66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TA210ST Super Tough PA66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super ToughnessInformation provided by E-Polymers Co. Ltd.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Water Absorption 1.2 %
1.2 %
23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D786
Tensile Strength, Yield 52.0 MPa
7540 psi
ASTM D638
Elongation at Break 80 %
80 %
ASTM D638
Flexural Yield Strength 75.0 MPa
10900 psi
ASTM D790
Flexural Modulus 1.80 GPa
261 ksi
ASTM D790
Izod Impact, Notched 9.00 J/cm
16.9 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 75.0 µm/m-°C

@Temperature 20.0 °C
41.7 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
Melting Point 260 °C
500 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Processing Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F