ExxonMobil LDPE LD 317.09 Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 317.09 Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 317.09 resin is a fractional melt index, 6% vinyl acetate copolymer film resin. Film made from LD 317.09 offers excellent impact strength, tensile properties and heat sealability.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Agriculture FilmBatch Inclusion BagsCoextrusion FilmsConstruction FilmForm Fill and Seal PackagingFreezer FilmHeavy Duty BagsIce BagsPoultry BagProduce BagsInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ExxonMobil method
Vinyl Acetate Content 6.0 %
6.0 %
ExxonMobil Method
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 620 %
620 %
ASTM D882
Elmendorf Tear Strength MD 130 g
130 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Dart Drop Test 490 g
1.08 lb
ASTM D1709A
Film Tensile Strength at Break, MD 32.4 MPa
4700 psi
ASTM D882
Film Tensile Strength at Break, TD 31.7 MPa
4600 psi
ASTM D882
1% Secant Modulus, MD 124 MPa
18000 psi
ASTM D882
1% Secant Modulus, TD 145 MPa
21000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 216 °C
<= 421 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 6.1 %
6.1 %
ASTM D1003
Gloss 66 %
66 %
45°; ASTM D2457