Huntsman PE1903 EVA Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1903 EVA Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
9% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent toughness and flexibility at low temperatures, and good heat-seal response.Applications: Film extrusion: laminating film, controlled atmosphere, heavy duty packaging, and medical tubingFDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 42
42
ASTM D2240
Tensile Strength, Ultimate 12.0 MPa
1740 psi
ASTM D638
Tensile Strength, Yield 7.00 MPa
1020 psi
ASTM D638
Film Elongation at Break, MD 325 %
325 %
ASTM D882
Film Elongation at Break, TD 475 %
475 %
ASTM D882
Elongation at Break 1200 %
1200 %
ASTM D638
Modulus of Elasticity 0.124 GPa
18.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.0930 GPa
13.5 ksi
ASTM D882
Secant Modulus, TD 0.104 GPa
15.1 ksi
ASTM D882
Dart Drop 13.0 g/micron
330 g/mil
ASTM D1709
Dart Drop Test 330 g
0.728 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 76.0 °C
169 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.5 %
4.5 %
ASTM D1003
Gloss 78 %
78 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 182 - 193 °C
360 - 379 °F