- Polymer Property : Tensile Strength, Yield = 1020 psi
Polymer Property : Tensile Strength, Yield = 1020 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 7.03 MPa | 1020 psi | ASTM D412 |
| Polymax® Maxelast® C4960 TPE, Transparent Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsSporting GoodsWire & Cable ElectronicsMedical DevicesPlastic TougheningInf.. |
|||
| Tensile Strength, Yield | 7.03 MPa | 1020 psi | ASTM D412 |
| Polymax® Maxelast® S4775 TPE, PS Overmold Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesSporting GoodsInformation from Alliance Polymers & Services, Distributor of Nantong .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527 |
| Polimeri Europa Greenflex® ML 20 Ethylene Vinyl Acetate Copolymer - Injection Molding Greenflex ML 20 is an ethylene vinyl acetate copolymer (EVA) for injection molding, when a good ESCR is required.Main Applications: Greenflex ML 20 is recommended for the production of flexible ite.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering F60A Fluorosilicone Rubber Blue Fluorosilicone, 56-65 °IRHD. Fluorosilicone rubber having methyl, vinyl and fluorine substituent groups on the polymer chain. To meet Aerospace Specification Mil-R-25988B, Class 1, Grade 60... |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering N65H Nitrile Rubber Nitrile Butadiene Rubber (NBR), 65-75 °IRHD. High acrylonitrile (ACN) content = 40% plus. Copolymer of acrylonitrile and butadiene.Applications: The high acrylonitrile content of this compound inc.. |
|||
| Tensile Strength, Yield | 7.00 - 13.0 MPa | 1020 - 1890 psi | ±30% change after 70 hours @ 100°C; ASTM D412 |
| Precision Polymer Engineering N80V Nitrile Rubber Nitrile/PVC Rubber, 75-85 °IRHD. Copolymer of acrylonitrile and butadiene, blended with PVC. ASTM & ISO designation = NBR.Applications: Excellent resistance to petroleum based oils and fuels. Impr.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering N90L Nitrile Rubber Low Nitrile Rubber, 85-95 °IRHD. Low acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. ASTM designation = NBR. ISO designation = NBR. ASTM D2000 line call-out M6BG907, A14, B.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering S50D Silicone Rubber Black Silicone Rubber, 46-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated to meet UK Ministry of Defence Aircraft Materials Specificatio.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering V75V Fluoroelastomer Compound Special steam resistant, Fluoroelastomer Rubber, 70-80 °IRHD. Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene. To meet ASTM D2000 line call-out MHK707, A1-10, B37, E.. |
|||
| Tensile Strength, Yield | 7.03 MPa | 1020 psi | At 100% elongation, across flow; ASTM D412 |
| Advanced Elastomer Systems VistaFlex® 911-B Thermoplastic Rubber
(discontinued **) Description: A black high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as free-f.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D638 |
| Huntsman PE1903 EVA Film Extrusion
(discontinued **) 9% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent toughness and flexibility at low temperatures, and good heat-seal response.Applications: Film extrusion: laminating film, controll.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| LyondellBasell Lupolen® V 3510 K Ethylene Vinyl Acetate, lnjection Molding Grade Injection moldingsData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| LyondellBasell Lupolen® V 3520 K Ethylene Vinyl Acetate Films, blow moldings.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 20.0 % |
1020 psi @Strain 20.0 % |
DIN 53504 |
| Huntsman IROGRAN® A 95 K 4640 TPU-For Seals Introduction: IROGRAN A95K 4640 is a caprolactone-based thermoplastic polyurethane. The material has been developed for injection molding applications requiring exceptional performance in terms of c.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 7.03 MPa | 1020 psi | 100%; ASTM D412 |
| Teknor Apex APEX® 3080-H Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Good FlexibilityUses-General Purpose, ProfilesAppearance-Natural Color, OpaqueForms-PelletsProcessin.. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Sibur BK-1675N Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For production of automobile inner tubes, heating tubes, sharper vulcanizer diaphragms, and rubber fabrics. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Commercial Neoprene® C653 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H608 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg T528 Butyl Rubber Butyl rubber is a copolymer of isobutylene and a small percentage of isoprene.PropertiesWith careful compounding Butyl has really good tensile strength.Butyl has very low permeability to air and oth.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H606 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 100 % |
1020 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® DP 8792A S043 Polyurethane PreprocessingMax. Water content |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKH 911 R PVC, Soft Extrusion Grade NAKAN FKH 911 R is a soft polyvinyl chloride compound developed for insulation automotive standard.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 810 R PVC, Soft Extrusion Grade NAKAN FKS 810 R is a soft polyvinyl chloride compound developed for insulation and sheathing.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527-2 |
| Arkema Group OREVAC® 18302N Maleic Anhydride Modified Linear Low Density Polyethylene OREVAC® 18365 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1010 VN 3 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for flexible, transparent films with high mechanical properties. Examples: stretch film, food packaging.ISO data provided by t.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 902 R PVC, Soft Extrusion Grade NAKAN FKS 902 R is a soft polyvinyl chloride compound developed for medium voltage hard insulation.ISO data provided by the manufacturer, Arkema. |
|||