Ineos B53-35H-100 HDPE

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Ineos Olefins & Polymers USA
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos B53-35H-100 HDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
B53-35H-100 is a high density polyethylene copolymer developed for injection blow molding. Zinc Stearate is incorporated in the formulation as a release agent. It is recommended for use in applications which require a combination of high top load strength and good environmental stress crack resistance (ESCR). This material meets the Food and Drug Administration requirements of 21CFR 177.1520.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ASTM D4883
Melt Flow 0.33 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.33 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 65
65
ASTM D2240
Tensile Strength, Yield 27.6 MPa
4000 psi
2 in/min (50 mm/min); ASTM D-638
Elongation at Break >= 700 %
>= 700 %
2 in/min (50 mm/min); ASTM D-638
Flexural Modulus 0.690 GPa
100 ksi
ASTM D747
1.241 GPa
180.0 ksi
Tangent-Method 1; ASTM D790
Izod Impact, Notched 3.40 J/cm
6.37 ft-lb/in
ASTM D256
Tensile Impact Strength 277 kJ/m²
132 ft-lb/in²
ASTM D1822
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 74.0 °C
165 °F
ASTM D648
Vicat Softening Point 131 °C
268 °F
ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746