LATI LARIL 13 Light Brown Polyphenylene Oxide (PPOm)  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LARIL 13 Light Brown Polyphenylene Oxide (PPOm)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most important properties featured by the Larils which can therefore be used within a wide range of temperatures (-40°C / +110°C). The Larils feature exceptional resistance to hydrolysis and are therefore applicable also in contact with very hot water. Specific Notes for this Material: light brown natural color; good dimensional stability; good impact resistance even at low temperatures. Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Water Absorption 0.060 %
0.060 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
LATI
Mechanical Properties Metric English Comments
Hardness, Rockwell M 84
84
ASTM D785
Tensile Strength, Ultimate 66.0 MPa
9570 psi
ISO 527
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ISO 527
33.0 MPa

@Temperature 90.0 °C
4790 psi

@Temperature 194 °F
ISO 527
46.0 MPa

@Temperature 60.0 °C
6670 psi

@Temperature 140 °F
ISO 527
Flexural Modulus 2.35 GPa
341 ksi
ASTM D790
2.06 GPa

@Temperature 120 °C
299 ksi

@Temperature 248 °F
ASTM D790
2.15 GPa

@Temperature 90.0 °C
312 ksi

@Temperature 194 °F
ASTM D790
2.25 GPa

@Temperature 60.0 °C
326 ksi

@Temperature 140 °F
ASTM D790
Izod Impact, Notched 2.00 J/cm

@Temperature 23.0 °C
3.75 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact Unnotched >= 30.0 J/cm²

@Temperature -20.0 °C
>= 143 ft-lb/in²

@Temperature -4.00 °F
DIN 53453
>= 30.0 J/cm²

@Temperature -40.0 °C
>= 143 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
>= 30.0 J/cm²

@Temperature 23.0 °C
>= 143 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
ASTM D648
Vicat Softening Point 130 °C
266 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Oxygen Index 22 %
22 %
ISO 4589
Glow Wire Test 750 °C

@Thickness 2.00 mm
1380 °F

@Thickness 0.0787 in
IEC 695-2-1
Electrical Properties Metric English Comments
Dielectric Strength 22.0 kV/mm

@Thickness 2.00 mm
559 kV/in

@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index 250 V
250 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Requested for non-reinforced self-extinguishing types. Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Requested for non-reinforced self-extinguishing types. Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) Y
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed medium - high
Needle Burner Test N
1.47 mm
N
3.05 mm