LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled
Manufacturer LATI
Trade Name Later
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
60.0 MPa

@Temperature 120 °C
 8700 psi

@Temperature 248 °F
80.0 MPa

@Temperature 90.0 °C
 11600 psi

@Temperature 194 °F
110 MPa

@Temperature 60.0 °C
 16000 psi

@Temperature 140 °F
150 MPa

@Temperature 23.0 °C
 21800 psi

@Temperature 73.4 °F
Elongation at Break 1.0 %

@Temperature 23.0 °C
 1.0 %

@Temperature 73.4 °F
1.3 %

@Temperature 60.0 °C
 1.3 %

@Temperature 140 °F
1.5 %

@Temperature 90.0 °C
 1.5 %

@Temperature 194 °F
1.7 %

@Temperature 120 °C
 1.7 %

@Temperature 248 °F
2.0 %

@Temperature 150 °C
 2.0 %

@Temperature 302 °F
Tensile Modulus 4.70 GPa

@Temperature 150 °C
 682 ksi

@Temperature 302 °F
6.20 GPa

@Temperature 120 °C
 899 ksi

@Temperature 248 °F
9.30 GPa

@Temperature 90.0 °C
 1350 ksi

@Temperature 194 °F
15.5 GPa

@Temperature 60.0 °C
 2250 ksi

@Temperature 140 °F
21.5 GPa

@Temperature 23.0 °C
 3120 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 225 °C

@Load 5.00 kg
 437 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 40 ohm
40 ohm
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa