LATI Laticonther 88/10 GR/50 PEEK, 50% Graphite Reinforced

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer	LATI
Trade Name	Laticonther
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Laticonther 88/10 GR/50 PEEK, 50% Graphite Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High thermal conductivity product based on Polyetheretherketone (PEEK). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.65 g/cc	0.0596 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Linear Mold Shrinkage, Transverse	0.0060 - 0.010 cm/cm	0.0060 - 0.010 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	70.0 MPa	10200 psi
Elongation at Break	0.50 %	0.50 %
Tensile Modulus	19.6 GPa	2840 ksi
Charpy Impact Unnotched	0.900 J/cmÂ²	4.28 ft-lb/inÂ²
Charpy Impact, Notched	0.300 J/cmÂ²	1.43 ft-lb/inÂ²

Thermal Properties	Metric	English	Comments
Thermal Conductivity	10.0 W/m-K	69.4 BTU-in/hr-ftÂ²-Â°F	Longitudinal
Deflection Temperature at 0.46 MPa (66 psi)	>= 300 Â°C	>= 572 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	>= 300 Â°C	>= 572 Â°F
Vicat Softening Point	>= 300 Â°C @Load 5.00 kg	>= 572 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	500000 ohm	500000 ohm

Processing Properties	Metric	English
Melt Temperature	380 - 400 Â°C	716 - 752 Â°F
Mold Temperature	180 - 190 Â°C	356 - 374 Â°F
Drying Temperature	150 - 170 Â°C @Time 10800 sec	302 - 338 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa