LATI Latilub 88/50-20T PEEK, PTFE Filled

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 88/50-20T PEEK, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0090 - 0.013 cm/cm
0.0090 - 0.013 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.014 cm/cm
0.010 - 0.014 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
Elongation at Break 30 %
30 %
Elongation at Yield 7.0 %
7.0 %
Tensile Modulus 3.90 GPa
566 ksi
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Coefficient of Friction, Dynamic 0.23
0.23
Coefficient of Friction, Static 0.26
0.26
K (wear) Factor 4.40 x 10-8 mm³/N-M
2.18 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point 270 °C

@Load 5.00 kg
518 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 360 - 390 °C
680 - 734 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa