LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer LATI
Trade Name Latiohm
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semiconductive/dissipative product based on Modified Polyphenylene Oxide (PPOm). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.192 g/cc
0.04306 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0035 cm/cm
0.0020 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0035 - 0.0050 cm/cm
0.0035 - 0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
Elongation at Break 1.0 %
1.0 %
Tensile Modulus 8.40 GPa
1220 ksi
Charpy Impact Unnotched 1.00 J/cm²
4.76 ft-lb/in²
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Vicat Softening Point 155 °C

@Load 5.00 kg
311 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 52 ohm-cm
52 ohm-cm
Surface Resistance 39 ohm
39 ohm
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Drying Temperature 80.0 - 100 °C

@Time 10800 sec
176 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa