LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ASTM D638
Tensile Modulus 12.7 GPa
1840 ksi
ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
Flexural Modulus 11.3 GPa
1640 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm

@Thickness 3.18 mm
1.30 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.06 J/cm

@Thickness 3.18 mm
7.61 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 9.70 kJ/m²
4.62 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 31.2 kJ/m²
14.8 ft-lb/in²
ISO 180
Falling Dart Impact 8.70 J
6.42 ft-lb
ASTM D3763
Impact Test 2.66 J
1.96 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 23.0 µm/m-°C

@Temperature 20.0 °C
12.8 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 45.0 µm/m-°C

@Temperature 20.0 °C
25.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
514 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 - 321 °C
601 - 610 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi