Lehmann & Voss LUVOCOMÂ® 2205-7054 Blend based on polyaryl ether ketone, with glass fiber

Category	Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® 2205-7054 Blend based on polyaryl ether ketone, with glass fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: High dimensionally stable precision parts, high continuous use temperature.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceChemical and hydrolysis resistance parts.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.55 g/cc	1.55 g/cc	ISO 1183
Linear Mold Shrinkage	0.0030 - 0.0070 cm/cm	0.0030 - 0.0070 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	115 MPa	16700 psi
Elongation at Yield	1.5 %	1.5 %
	2.0 %	2.0 %	flexural
Modulus of Elasticity	10.0 GPa	1450 ksi
Flexural Strength	160 MPa	23200 psi
Flexural Modulus	8.00 GPa	1160 ksi
Charpy Impact Unnotched	4.00 J/cmÂ²	19.0 ft-lb/inÂ²	edgewise; ISO 179 1eU

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	220 Â°C	428 Â°F
	250 Â°C	482 Â°F	short term

Electrical Properties	Metric	English	Comments
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	390 Â°C	734 Â°F	mass temp
Nozzle Temperature	360 - 380 Â°C	680 - 716 Â°F
Zone 1	360 - 370 Â°C	680 - 698 Â°F
Zone 2	370 - 380 Â°C	698 - 716 Â°F
Zone 3	380 - 390 Â°C	716 - 734 Â°F
Mold Temperature	160 - 200 Â°C	320 - 392 Â°F
Drying Temperature	150 Â°C @Time 10800 - 21600 sec	302 Â°F @Time 3.00 - 6.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	blue