Multibase Multi-Pro® 4006 T H BLK 40% Talc Content Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer Multibase
Trade Name Multi-Pro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Pro® 4006 T H BLK 40% Talc Content Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Multi-Pro 4002 T H is a talc reinforced polypropylene compound with excellent stiffness at medium impact resistance. Its heat resistance is improved over natural and can resist 150°C for 750 hours in an accelerated oven aging test. This product meets CMP PP 010 specifications.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792-91
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM D955-89
Melt Flow 5.0 g/10 min
5.0 g/10 min
(Condition L) ASTM D-1238-94a
Mechanical Properties Metric English Comments
Hardness, Shore D 77
77
10 sec; ASTM D-2240-95
Tensile Strength, Ultimate 30.3 MPa
4390 psi
ASTM D638-95
Elongation at Break 25 %
25 %
ASTM D638-95
Flexural Modulus 3.276 GPa
475.2 ksi
Secant 20% strain; ASTM D-790-95
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256-93a
Gardner Impact 0.700 J
0.516 ft-lb
ASTM D5420-93
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
244 °F
ASTM D648-95
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
ASTM D648-95