- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 147 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 147 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648-95 |
| Multibase Multi-Pro® 4006 T H BLK 40% Talc Content Polypropylene Multi-Pro 4002 T H is a talc reinforced polypropylene compound with excellent stiffness at medium impact resistance. Its heat resistance is improved over natural and can resist 150°C for 750 hours.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ASTM D648 |
| RheTech Products M15P101-01A 15% Mica Reinforced Polypropylene, Black Applications: Air ducts - distributionFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Ovation Polymers Opnyl OP66UT108 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 75/Method Af |
| Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound PRE-ELEC® PP 1396 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
| Eastman Eastar GN005 Copolyester, Natural
(discontinued **) Eastar GN005 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN005 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
| Eastman 9921P PET Injection Molded
(discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman EASTALLOY Polymer DA003-8999K, Clear Alloy
(discontinued **) Properties below based on a film thickness of 250 microns. CO2 Permeability is 49 cm3·mm/m2·24h·atm per ASTM D 1434.Product Description: EASTALLOY DA003-8999K Polymer is a clear copolyester/pol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9001-16H , 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 - 248 °C | 147 - 478 °F | Average value: 99.6 °C Grade Count:41 |
| Overview of materials for Nylon 66, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL V081 PPE+HIPS (Europe-Africa-Middle East) NORYL V081 is a high flow, UV stabilized PPO/PS blend for TV backplate applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 55T1030 PP SABIC® PPcompound 55T1030 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact, and is suitable for multiple processing met.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| SK Chemicals SKYGREEN® PETG 2008 Specially Formulated PET Copolymer Resin SKYGREEN PETG is an amorphous copolyester in which a certain amount of ethylene glycol is replaced with 1,4-cyclohexane dimethanol (CHDM), which prevent crystallization, leading to improved processa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
| Borealis PS65T20 Polypropylene Compound, Mineral Filled PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection molding. This material has excellent balanced mechanical properties and high melt flow rate. Applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
| Eastman Drystar 0113 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman Drystar 0601 Copolyester, Injection Molded This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman Eastar DN011 Copolyester Eastar Copolyester DN011 is a brilliantly clear polymer having excellent impact strength, chemical resistance, and low shrinkage rates. Eastar Copolyester DN011 contains a mold release.Applications/.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 285A2R30023 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 530E3720010 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ HMU 208 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness and release agent for automotive HVAC and under-the-hood applications.Availability: Africa & Middl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ HMU 234 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness, high heat stabilization, low emissions and low odor for automotive HVAC and under-the-hood applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starpylen HU 70E3 HDPE, Injection Molding Starpylen HU 70E3 is a High Density Polypropylene Injection Molding Resin (also known as HU70E3)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334W20L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 152 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® ST801 NC010A Nylon 66
(Unverified Data**) Zytel® ST801 is an unreinforced, super tough polyamide 66 for injection molding and extrusion. It offers outstanding break resistance over a wide temperature and humidity range and high productivit.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 - 88.0 °C | 147 - 190 °F | Average value: 75.8 °C Grade Count:74 |
| Overview of materials for Cellulose Acetate Propionate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
| 3M Dyneon™ PVDF 60512/0000 Polyvinylidene Fluoride
(discontinued **) Polyvinylidenefluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and.. |
|||