NOVA Chemicals Novapol® TD-9055-E Hexene LMDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® TD-9055-E Hexene LMDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of cast film extruded at 280°C.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.938 g/cc
0.0339 lb/in³
ASTM D792
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 15.0 MPa
2180 psi
ASTM D882
Film Tensile Strength at Yield, TD 16.0 MPa
2320 psi
ASTM D882
Film Elongation at Break, MD 800 %
800 %
ASTM D882
Film Elongation at Break, TD 1070 %
1070 %
ASTM D882
Secant Modulus, MD 0.320 GPa
46.4 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.380 GPa
55.1 ksi
at 1%; ASTM D882
Impact 80
80
J/mm; NOVA Chemicals Puncture test
Coefficient of Friction >= 0.80
>= 0.80
ASTM D1894
Elmendorf Tear Strength, MD 1.40 g/micron
35.6 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 8.00 g/micron
203 g/mil
ASTM D1922
Film Tensile Strength at Break, MD 41.0 MPa
5950 psi
ASTM D882
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ASTM D882
Optical Properties Metric English Comments
Haze 4.0 %
4.0 %
ASTM D1003
Gloss 87 %
87 %
at 45°; ASTM D2457