Polymer Property : Density = 0.938 g/cc Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
Polimeros Mexicanos Rotolene® 93835-TG Medium Density Polyethylene MDPE Copolymer with UV8 stabilizer in natural and colors.Recommended for rotomolding. Used for manufacture of water tanks > 2000 liters, cisterns, farm tanks, or tanks to contain strong acids and b..
Density	0.938 - 0.942 g/cc	0.0339 - 0.0340 lb/in³	Base Resin; ASTM D1505
NIZHNEKAMSKNEFTEKHIM PE 4440R (40404) Medium Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
NOVA Chemicals Novapol® TD-9055-E Hexene LMDPE Film Resin Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of cast film extruded at 280°C.Information provided by NOVA Chemicals..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D 792
NOVA Chemicals Novapol® TF-0438-E Hexene LMDPE Film Resin TF-0438-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
NOVA Chemicals Novapol® TI-0338-A MDPE Masterbatch Resin Molded Plaque Properties. Features: Hexene Copolymer, excellent impact strength, excellent ESCR.Applications: large parts, agricultural storage tanks.Data provided by the manufacturer.
Density	0.938 g/cc	0.0339 lb/in³	ASTM D4883
ExxonMobil LL 8401.67 Rotational Molding Resin (discontinued **) LL 8401 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for Non-UV applications that require optimum balance of flow processabil..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D4883
ExxonMobil Escorene® LL-8461 LLDPE, Rotational Molding Powder (discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good stiffnessUses: Septic tanks, Chemical storage bins, Potable water tanks
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, ..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
NOVA Chemicals Novapol® TR-0338-U MDPE Rotational Molding Resin (discontinued **) Molded Plaque Properties. Features: Hexene Copolymer, excellent impact strength, excellent ESCR.Applications: large parts, agricultural storage tanks.Data provided by the manufacturer.
Density	0.938 g/cc	0.0339 lb/inÂ³
LyondellBasell LupolenÂ® 3822 D GB 00350 MDPE Data was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.
Density	0.938 g/cc	0.0339 lb/inÂ³	Natural; ASTM D4883
Ineos TUB 172 HDPE TUB 172 is a yellow medium density polyethylene copolymer designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stress life and slow crack growth resistance. T..
Density	0.938 g/cc	0.0339 lb/inÂ³	ASTM D792
Lushan L-5R (HC) Polyethylene Copolymer Adhesive for Steel Pipe Coating Copolymer adhesive resin Lushan L-5R series is maleic anhydride grafted polyethylene which could be in granule or powder form. It was developed by Lushan with independent patent technologies and pro..
Density	0.938 g/cc	0.0339 lb/inÂ³	ASTM 1505-68
Iran Petrochemical (PCC) 3840 UA Medium Density Polyethylene MD3840UA is a linear medium density polyethylene (MDPE) with butene copolymer. This polymer has good impact strength, excellent external and internal surface finish, whiteness, good stress cracking ..
Density	0.938 g/cc	0.0339 lb/inÂ³	ISO 1872/1
SIDPEC EGYPTENEÂ® HD 3840 EA MDPE Wire and Cable Grade Applications:Suitable for the production of silane cross-linkable compoundsLow voltage power cable insulationInjection molded technical parts and closureInformation provided by Interchim s.r.l., off..
Density	0.938 g/cc	0.0339 lb/in³	ISO 1183
Unipetrol PE HD LITEN® FB/FL 20 HDPE Made for tubular film and special applications.Information provided by Unipetrol RPA
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792
DuPont Appeel® LSR20D745 Lidding Sealant Resin Appeel® LSR20D745 is a modified ethylene acrylate resin designed to function as a sealing layer for lidding applications. It is most often suggested to provide peelable seals over a broad temperatu..
Density	0.938 g/cc	0.0339 lb/in³	Base Density; ASTM D1505
Chevron Phillips Marlex® M358Y3 LLDPE Pipe and Corrugated Extrusion Resin Characteristics: High visibility as gas pipingGood outdoor storage length when blended with natural MDPE containing UV stabilizerGood long-term hoop strengthApplications: PipesNot recommended for co..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D792, ISO 1183
DuPont™ Bynel® 30E753 Anhydride Modified Ethylene Vinyl Acetate BYNEL® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D4883
ExxonMobil LL 8460.29 Rotational Molding Resin Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D4883
ExxonMobil LLP8460.29 Rotational Molding Resin Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance o..
Density	0.938 g/cc	0.0339 lb/in³
Dow Primacor® 3460 Ethylene Acrylic Acid (EAA) PRIMACOR® 3460 polymer containing 9.5% comonomer is a heat seal coating for high speed packaging applications where low temperature processing is necessary for minimal taste and odor effects. It is..
Density	0.938 g/cc	0.0339 lb/in³	ExxonMobil Method
ExxonMobil Escorene® UL 7520 Adhesive Application Resin Escorene Ultra UL 7520 is a high flow, 18.5% vinyl acetate copolymer that has very good compatibility with hydrocarbon tackifiers and most waxes. It is suitable for making hot melt adhesives, sealan..
Density	0.938 g/cc	0.0339 lb/in³	ExxonMobil method
ExxonMobil Escorene™ FL 01418 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 01418 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 01418 is an excellent sealing materi..
Density	0.938 g/cc	0.0339 lb/in³
Dow Primacor® 1410 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
Density	0.938 g/cc	0.0339 lb/in³
Dow Primacor® 1420 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical.
Density	0.938 g/cc	0.0339 lb/in³	ASTM D1505
Arkema Group OREVAC® 9314 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..
Density	0.938 g/cc	0.0339 lb/in³	ASTM D1505
PolyOne Syncure™ S1027A Polyethylene, Crosslinked (XLPE) Moisture Crosslinkable Polyethylene Compound. Available as Base Resin component for PolyOne Syncure System.Tensile, Oven Aging, measured on a 100 phr S1027A / 20 phr V0022G system. Deformation, Hot ..
Density	0.938 - 2.56 g/cc	0.0339 - 0.0925 lb/in³	Average value: 1.15 g/cc Grade Count:281
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri..