NOVA Chemicals Sclair® FP020-D Octene Copolymer LLDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® FP020-D Octene Copolymer LLDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FP020-D complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. FP020-D is subject to the specific limitation that it may contact food only at temperatures of 212°F and below.NOVA Chemicals' polyethylene resins are chemically and biologically inert.Features: Outstanding toughness and strength, Excellent sealability, Low gelAdditives: Antioxidant, Polymer process aid, Antiblock, SlipApplications: Sealant and lamination film for food packaging, High strength filmProperties measured from blown film produced on a laboratory extruder with 4" die and a 35-mil die gap at a blowup ratio of 2.5:1, and melt temperature 420°F. Films were made from 100% FP020-D.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D 792
Thickness 25.0 microns
0.984 mil
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.80 MPa
1420 psi
ASTM D 882
Film Tensile Strength at Yield, TD 9.70 MPa
1410 psi
ASTM D 882
Film Elongation at Break, MD 500 %
500 %
ASTM D 882
Film Elongation at Break, TD 800 %
800 %
ASTM D 882
Elmendorf Tear Strength MD 370 g
370 g
ASTM D 1922
Elmendorf Tear Strength TD 650 g
650 g
ASTM D 1922
Elmendorf Tear Strength, MD 14.8 g/micron
376 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 26.0 g/micron
660 g/mil
Dart Drop Test 550 g
1.21 lb
22; ASTM D 1709/A
Film Tensile Strength at Break, MD 57.0 MPa
8270 psi
ASTM D 882
Film Tensile Strength at Break, TD 46.0 MPa
6670 psi
ASTM D 882
1% Secant Modulus, MD 180 MPa
26100 psi
ASTM D 882
1% Secant Modulus, TD 205 MPa
29700 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 10 %
10 %
ASTM D 1003
Gloss 58 %
58 %
at 45°; ASTM D 2457
Descriptive Properties Value Comments
Low Friction Puncture (J/mm) 60
NOVA Chemicals Test Method