Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Nickel Coated Graphite Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PEI, NCG Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.31 - 1.52 g/cc
0.0473 - 0.0549 lb/in³
Average value: 1.41 g/cc Grade Count:10
Filler Content 5.00 - 30.0 %
5.00 - 30.0 %
Average value: 17.5 % Grade Count:6
Water Absorption 0.0200 - 0.250 %
0.0200 - 0.250 %
Average value: 0.174 % Grade Count:5
Linear Mold Shrinkage 0.000100 - 0.00600 cm/cm
0.000100 - 0.00600 in/in
Average value: 0.00178 cm/cm Grade Count:10
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 114 - 165 MPa
16500 - 24000 psi
Average value: 137 MPa Grade Count:10
Elongation at Break 1.00 - 8.00 %
1.00 - 8.00 %
Average value: 2.65 % Grade Count:10
Modulus of Elasticity 5.52 - 14.5 GPa
800 - 2100 ksi
Average value: 10.9 GPa Grade Count:10
Flexural Yield Strength 179 - 221 MPa
26000 - 32000 psi
Average value: 200 MPa Grade Count:10
Flexural Modulus 5.52 - 15.2 GPa
800 - 2200 ksi
Average value: 10.2 GPa Grade Count:10
Izod Impact, Notched 0.374 - 0.694 J/cm
0.700 - 1.30 ft-lb/in
Average value: 0.502 J/cm Grade Count:10
Izod Impact, Unnotched 2.67 - 5.34 J/cm
5.00 - 10.0 ft-lb/in
Average value: 4.08 J/cm Grade Count:10
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 204 - 213 °C
400 - 415 °F
Average value: 208 °C Grade Count:8
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 ohm-cm - 1e+05
1.00 ohm-cm - 1e+05
Average value: 25.0 ohm-cm Grade Count:10
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
Average value: 185000 ohm Grade Count:10
Static Decay 0.500 - 2.00 sec
0.500 - 2.00 sec
Average value: 1.50 sec Grade Count:9
Processing Properties Metric English Comments
Processing Temperature 349 - 382 °C
660 - 720 °F
Average value: 366 °C Grade Count:6
Melt Temperature 354 - 399 °C
670 - 750 °F
Average value: 380 °C Grade Count:4
Mold Temperature 135 - 177 °C
275 - 350 °F
Average value: 156 °C Grade Count:10
Drying Temperature 149 °C
300 °F
Average value: 149 °C Grade Count:4
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:4
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:4
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi
Average value: 103 MPa Grade Count:10