Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 114 MPa | 16500 psi | ASTM D638 |
Custom Resins Vexel™ E20GF15 , 15% Glass Reinforced PET
(discontinued **) Description: Vexel™ E20GF15 is a 15% glass fiber reinforced, general purpose PET. Information provided by Custom Resins. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® SF-35GF-15MC/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® SF-35GF-25MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedUL 94 V0 (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 114 - 145 MPa | 16500 - 21000 psi | Average value: 131 MPa Grade Count:8 |
Overview of materials for Nylon 12, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | ASTM D638 |
Global GPEI-210 10% Glass Filled Reinforced, Polyetherimide Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | |
MTI ThermoStran® PP-50G Long Glass Fiber Compound ThermoStran® is custom designed long fiber thermoplastic compound (LFC) engineered to meet specific end use requirements. Continuous fibers are pultruded to yield pellets with fibers equivalent t.. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 610 Nylon 6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | 5 mm/min |
Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLS,16-050,(G+C)(F+D)(30+05)Rigid grade with glass fiber (30%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab.. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | ASTM D638 |
Chem Polymer Durlex 730 GVH PBT, 30% Glass Fiber Reinforced A glass fiber reinforced, flame retardant PBT exhibiting excellent strength, dimensional stability and elevated temperature performance. The material has a V0 flammability rating according to UL94 .. |
|||
Tensile Strength, Ultimate | 114 - 165 MPa | 16500 - 24000 psi | Average value: 137 MPa Grade Count:10 |
Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "PEI, NCG Filled". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | |
Phenolic 40%, Carbon fabric 60% Phenolic - Monsanto "SC 1008". Carbon fabric - "CCA-1" |
|||
Tensile Strength, Ultimate | 114 MPa | 16500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® SF-35GF-25MN/000 L Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |