Polymer Property : Flexural Modulus = 8.40 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
NHEP Spectron™ E5469 Nylon 66, 33% Glass Fiber Natural color. E5469 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informat..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
NHEP Spectron™ E6666 Nylon 66, 30% Glass Fiber Natural color. E6666 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati..
Flexural Modulus	8.40 GPa	1220 ksi	ISO Value
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
Plenco Valite 759 Novolac Phenolic, Granular, Injection Molded (discontinued **) This Valite product has been replaced by Plenco 4759. Data provided by Plenco.VALITE 759 is a black, two stage, medium heat resistant phenolic molding compound. It has excellent molded finish and p..
Flexural Modulus	8.40 GPa	1220 ksi	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AKV 30 000000 Nylon 66, Glass Fiber Reinforced PA 66, 30% glass fibers, injection moldingInformation provided by LANXESS.
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178
Solvay TechnylÂ® A 218 V30 Nylon 66, 30% Glass Fiber, EH0 Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and..
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178
Solvay TECHNYLÂ® C 218 V 30 PA6, 30% glass fiber, DRY Description: TECHNYLÂ® C 218 V30 is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers..
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178
Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTARâ„¢ S 218 V30 is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is..
Flexural Modulus	8.40 GPa	1220 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 771 PBT (Europe-Africa-Middle East) VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin.
Flexural Modulus	8.40 GPa	1220 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon EE002ER PEI (Europe-Africa-Middle East) LNP* Lubricomp* EFP36G is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.This data wa..
Flexural Modulus	8.40 GPa	1220 ksi
SPS Guang Zhou POBUXâ„¢ 3001G30 Flame-retarded/GF30%-PBT Characteristic: Good flame retardance, high mechanical properties, high rigidity, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) ..
Flexural Modulus	8.40 GPa	1220 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic.
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific) PPE+PS, Noryl, Glass Fiber, Mica, Flame Retardant, UL Grade, Non-Halogen Flame Retaardant, High Flow,
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178
Solvay TECHNYLÂ® A 216 V30 PA66, 33% glass fiber, DRY Description: Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: TECHNYL A 216 V30 is ..
Flexural Modulus	8.40 GPa	1220 ksi	At 2 mm/min; ISO 178
Borealis Nepol™ GB402HP 40% Long Glass Fiber Reinforced Polypropylene Nepol GB402HP is a 40% long glass fiber reinforced polypropylene grade, produced using Borealis ` propriety and exclusive, patented Nepol technology intended for injection molding and extrusion. Th..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
Plenco 3509 Phenolic, Granular, Injection Molded PLENCO 03509 is a mineral and flock filled phenolic molding compound offering excellent electrical properties, dimensional stability, and improved heat resistance. UL recognized under component file..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
Plenco 4327 Phenolic, Granular, Compression Molded PLENCO 04327 is a heat resistant mineral filled phenolic molding compound offering excellent cosmetic characteristics and improved heat resistant properties. PLENCO 04327 is not intended for electri..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
Plenco 6582 Phenolic, Briquette, Injection Molded PLENCO 06582 is a rubber modified phenolic molding compound, offering excellent heat resistant properties, along with improved mechanical strength at elevated temperatures. UL recognized under compo..
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178-93
Wellman Wellamid® MRGFX1716-BK1 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6 Description: Mineral/Glass Reinforced, Silicone Lubricated Nylon 6Information provided by Wellman.
Flexural Modulus	8.40 GPa	1220 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6600 GV 30 HWCP 30% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	8.40 GPa	1220 ksi	ISO 178
DuPont Performance Polymers Crastin® LW9330 NC010 PBT+SAN (Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9330 NC010 is a 30% glass fiber reinforced polybutylene terephthalate blend for injection molding. I..
Flexural Modulus	8.40 GPa	1220 ksi	DAM; ISO 178
DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612 (Unverified Data**) 33% Glass Reinforced Polyamide 612 Developed for Electrical and Electronics Applications Zytel FE5382 BK276 is a 33% glass fiber reinforced heat stabilized black polyamide 612 resin developed for el..
Flexural Modulus	8.40 GPa	1220 ksi	2 mm/min; ISO 178
Eurostar Starflam RF0055E PA66/6, 25% Glass Filled, Injection Molded Starflam RF0055E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z250EM)Information provided by Polym..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced for extrusion applications.Data provided by the manufacturer
Flexural Modulus	8.40 GPa	1220 ksi	ISO Data
BASF Ultramid® B3WGM24 BK30564 10/20% Glass/Mineral Filled PA6 (Dry) Ultramid B3WGM24 BK30564 is a 30% glass/mineral filled heat stabilized injection molding PA6 grade for industrial articles having medium to high rigidity and high dimensional stability.
Flexural Modulus	8.40 GPa	1220 ksi	ISO Data
BASF Ultramid® TG7S BK-102 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified nylon 6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushi..
Flexural Modulus	8.40 GPa	1220 ksi	ASTM D790
A. Schulman ComAlloy Hiloy® 623 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	8.40 GPa	1220 ksi	ISO Value
BASF Capron® HPN 9233G HS BK-102 33% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced nylon 6 injection molding grade resin in the High Productivity Nylon Series developed for improved cycle times ..