Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Riblene FM 50 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FM 50 is characterized by optimum optical properties and rigidity.Films manufactured with Riblene FM 50 are easily heat shrinkable.Main Applications: Riblene FM 50 is recommended for automatic packaging where low gauge films having a certain rigidity and gloss are required (hygienic packaging).Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.933 g/cc
0.933 g/cc
ISO 1183
Thickness 18.0 - 50.0 microns
0.709 - 1.97 mil
Recommended
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 14.0 MPa
2030 psi
ISO 527-3
Film Tensile Strength at Yield, TD 15.0 MPa
2180 psi
ISO 527-3
Film Elongation at Break, MD 350 %
350 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 5.095 g/micron
129.4 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 6.6235 g/micron
168.24 g/mil
ISO 6383-2
Dart Drop Test 80.0 g
0.176 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 21.0 MPa
3050 psi
ISO 527-3
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ISO 527-3
1% Secant Modulus, MD 300 MPa
43500 psi
ISO 527-3
1% Secant Modulus, TD 310 MPa
45000 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 118 °C
244 °F
Internal method
Vicat Softening Point 107 °C

@Load 1.00 kg
225 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Optical Properties Metric English Comments
Haze 7.5 %
7.5 %
ISO 14782
Gloss 72 %
72 %
45°; ASTM D2457