PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Optimum for Black and Darker Colors below 50L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Ductile/Brittle transition as measured by Instrumented Impact is 5 deg.C Physical properties based on Geon HTX Ultra LA425 Natural 0000Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 74
74
15 sec; ASTM D2240
Tensile Strength, Yield 37.9 MPa
5500 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 1.99 GPa
289 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 66.1 MPa
9590 psi
ASTM D790
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
Izod Impact, Notched 7.20 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
13.5 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 66.7 J/cm

@Temperature 23.0 °C
0.125 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
178 J/cm

@Temperature 23.0 °C
0.333 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.0 µm/m-°C
47.8 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 90.6 °C

@Thickness 3.18 mm
195 °F

@Thickness 0.125 in
Unannealed; ASTM D648
91.1 °C

@Thickness 3.18 mm
196 °F

@Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 83.9 °C

@Thickness 3.18 mm
183 °F

@Thickness 0.125 in
Unannealed; ASTM D648
87.2 °C

@Thickness 3.18 mm
189 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 174 - 193 °C
345 - 379 °F
Descriptive Properties Value Comments
Ease of Sizing Acceptable
Features Good Weather Resistance
High Impact Resistance
High Stiffness
Forms Pellets
Generic Material PVC Alloy
Generic Name Polyvinyl Chloride Alloy (PVC Alloy)
Processing Method Extrusion
PVC Cell Classification 15225
ASTM D1784
4-42411-64-0000
ASTM D4216