PolyOne Geon™ Specialty Suspension Atlas S140 Polyvinyl Chloride Homopolymer (PVC Homopolymer)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Specialty Suspension Atlas S140 Polyvinyl Chloride Homopolymer (PVC Homopolymer).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Geon® Atlas S140 is high molecular weight homopolymer specialty suspension resin intended for use in high strength extruded parts. It improves the physical performance of end application for intsance wire and cable insulation, extruded tubes. The high porosity property of this resin allows rapid plasticizer absorption reducing the compound cycle times and resulting in high compound throughput and low manufacturing cost. Geon® Atlas S140 improves heat distortion (HDT) performance, increase the strength for highly plasticized formulas, and provides longer product shelf life.Note: The value set forth represent 'typical' values and PolyOne Corporation, therefore, makes no representation that the material in any particular shipment will conform to the listed properties. Packaging: This resin is shipped in multi-wall paper bags, netweight 50lbs, 2,500lbs per pallet. Information shown on the package includes commercial identification number, lot, and weight. STP 488 (formulation): 100phr Geon® Atlas S140, 55phr TOTM, and 18phr Filler ASTM D638 (formulation): 100phr Geon® Atlas S140, 60phr DINP, 5phr ESO, and 2phr Mark 4716Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Volatiles 0.070 %
0.070 %
Geon® STP 793; Internal Method
Apparent Bulk Density 0.410 g/cc
0.0148 lb/in³
Geon® STP 1169; Internal Method
Porosity 0.57 %
0.57 %
cm³/g; Geon® STP 1094; Internal Method
Particle Size <= 105 µm
<= 105 µm
14.8%; Geon® DFT 1466; Internal Method
145 µm
145 µm
Average Particle SizeGeon® DFT 1466; Internal Method
>= 250 µm
>= 250 µm
3.4%; Geon® DFT 1466; Internal Method
Relative Viscosity 3.1 cP
3.1 cP
Correlation, Cyclohexanone 1%; Internal Method
Viscosity Measurement 1.4
1.4
Inherent; ASTM D1243-60-A
Mechanical Properties Metric English Comments
Tensile Strength 17.9 MPa
2600 psi
Optimum; With provided formulation; ASTM D638
Descriptive Properties Value Comments
Contamination 0
Internal Method; Magnetic ParticlesGeon® STP 1217 Unit: #/100in2
1
Internal Method; Dark ParticlesGeon® STP 1217 Unit: #/100in2
4
Internal Method; Light Colored ParticlesGeon® STP 1217 Unit: #/100in2
Features High Strength
Flow Time 27 sec
Internal Method; Conditioned Funnel Flow TimeGeon® STP 1169
Forms Powder
White powder
Generic Material PVC Homopolymer
Generic Name Polyvinyl Chloride Homopolymer (PVC Homopolymer)
K-Value 82
Internal Method; Correlation, 0.5g/100ml
Polymerization Process Suspension
Powder Mix Time 2.6 min
Internal Method; Geon® STP 488 with provided formulation
Processing Method Extrusion
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Residual Vinyl Chloride Monomer < 1 ppm
Internal Method; Geon® STP 1005
Uses Insulation
Wire & Cable Applications