Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 17.9 MPa | 2600 psi | ASTM D412 |
S&E Specialty Polymers GA-7056D-FR-105 PVC Application: 105° C Matt finish, FR, Lead Free, Phthalate Free PVC jacketing compound designed to be non-migratory to Styrene and polycarbonate base connectors.Information provided by S&E Specialty.. |
|||
Tensile Strength | >= 17.9 MPa | >= 2600 psi | ASTM D412 |
S&E Specialty Polymers TufFlex™ GA-509-80-5 TPE Compound Application: A Matte Finish, Flexible, Sunlight Resistant, 105?C Jacketing Compound with 60?C Oil Resistance.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 17.9 MPa | 2600 psi | ASTM D412 |
S&E Specialty Polymers TufTech™ GA-5062R PVC Compound Application: An 80°C rated, PVC based, highly flame retardant jacketing compound.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 17.9 MPa | 2600 psi | Optimum; FF; ASTM D638 |
PolyOne Geon™ 170 Series 179 Polyvinyl Chloride Homopolymer (PVC Homopolymer) Note: Plastisol Formulation F1 consists of 100 parts of this resin + 60 parts DOP. Note: Plastisol Formulation F2 consists of 100 parts of this resin + 57 parts DOP + 3 parts ESO + 2 parts Synpron®.. |
|||
Tensile Strength | 17.9 MPa | 2600 psi | Optimum; With provided formulation; ASTM D638 |
PolyOne Geon™ Specialty Suspension Atlas S140 Polyvinyl Chloride Homopolymer (PVC Homopolymer) Geon® Atlas S140 is high molecular weight homopolymer specialty suspension resin intended for use in high strength extruded parts. It improves the physical performance of end application for intsan.. |
|||
Tensile Strength | 17.9 MPa @Strain 100 % |
2600 psi @Strain 100 % |
Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV3859 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength | 17.9 MPa | 2600 psi | ASTM D412 |
S&E Specialty Polymers TufTech™ GA-8705-03A PVC Compound Application: 80°C Riser Jacketing Compound.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 17.9 MPa | 2600 psi | ASTM D412 |
S&E Specialty Polymers TufTech™ GA-93-016AGH PVC Compound Application: A RoHS Compliant, Flame Retardant 60/75?C Jacketing Compound.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 17.9 MPa | 2600 psi | ASTM D412 |
S&E Specialty Polymers TufTech™ GM-3285 PVC Compound Application: A clear, FDA grade, PVC extrusion compound for general non-toxic or 75°C rated wire applications.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 17.9 MPa | 2600 psi | Typical |
Garlock Viblonâ„¢ 256 Neoprene Bearing Pad Viblonâ„¢ pads are technically engineered and specifically designed to cushion impact, shock and vibration. Constructed of multiple layers of high-quality, cotton-polyester duck fabric, completel.. |
|||
Tensile Strength | 17.9 MPa | 2600 psi | Typical properties determined of film cast from toluene solution; ASTM D412 |
Kraton® D1193 P (SIS) Linear Triblock Copolymer Description: Kraton D1193 P is a clear, linear triblock copolymer based on styrene and isoprene, with a polystyrene content of 24%. It is supplied from North America in the physical form identified:.. |
|||
Tensile Strength | 17.9 MPa | 2590 psi | Average; ASTM D412 Method A |
Seals Eastern 7346 Extreme Low Temperature Service Rubber HNBR for cold temp (-50°C) and/or aqueous serviceInformation provided by Seals Eastern. |
|||
Tensile Strength | 17.9 MPa | 2600 psi | |
AlphaGary Garaflex™ G 7765-A5R Thermoplastic Elastomer Garaflex™ G is a thermoplastic elastomer intended for wire and cable applications105°C rated TPE for wire and cable applications including welding cables |
|||
Tensile Strength | 17.9 MPa | 2600 psi | |
AlphaGary GW 2403-1 VW1 105-LCF Flame Retardant Polyvinyl Chloride 105°C rated low temperature oil & sunlight resistant jacketing compound for tray cable application |
|||
Tensile Strength | 17.9 MPa | 2600 psi | |
AlphaGary GW 2326 A VW1 LCF Flame Retardant Polyvinyl Chloride 90°C rated low temperature jacket compound. |
|||
Tensile Strength | 17.9 MPa | 2600 psi | |
AlphaGary GW 2403-1 VW1 LCF Flame Retardant Polyvinyl Chloride 90°C rated jacket compound for tray cable, oil resistant |
|||
Tensile Strength | 17.9 MPa | 2600 psi | |
AlphaGary PVC FMPP - Clear, Various Colors Polyvinyl Chloride Thermoplastic Resistant to UV, moisture and mildew for high speed extrusion of coated yarn for outdoors furniture, wire fence coating and automotive harness cable coating |