PolyOne LubriOne™ ATH-05KV/000 Acetal (POM) Homopolymer  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne LubriOne™ ATH-05KV/000 Acetal (POM) Homopolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D792
Water Absorption 0.050 %

@Thickness 3.18 mm,
Time 86400 sec
0.050 %

@Thickness 0.125 in,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.020 - 0.023 cm/cm
0.020 - 0.023 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.2 MPa
8010 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 10 - 12 %
10 - 12 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.76 GPa
400 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 55.2 MPa
8010 psi
ASTM D790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic 0.46
0.46
vs. Steel; ASTM D1894
Coefficient of Friction, Static 0.45
0.45
vs. Steel; ASTM D1894
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C

@Thickness 6.35 mm
264 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C

@Thickness 6.35 mm
261 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 193 - 216 °C
379 - 421 °F
Descriptive Properties Value Comments
Features Good Wear Resistance
Homopolymer
Low Friction
Forms Pellets
Generic Name Acetal (POM) Homopolymer
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Appliance Components
Automotive Applications
Bearings
Business Equipment
Consumer Applications
Conveyor Parts
Gears
Industrial Applications
Printer Parts
Pulleys
Rollers