Polymer Property : Tensile Modulus = 2.76 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	2.76 GPa	400 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ Vinyl Rigid Extrusion 87775 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Tensile Modulus	2.76 GPa	400 ksi	ASTM D638
Quadrant EPP Acetron® POM-C Copolymer Acetal, Porosity-Free, Unfilled, Extruded
Tensile Modulus	2.76 GPa	400 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ Vinyl Dry Blend E6755 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Tensile Modulus	2.76 - 3.10 GPa	400 - 450 ksi	ASTM D790
Alcoa KAMA 2200 Prime Graphic Arts OPS (discontinued **) CapabilitiesGauge: .001” to .004” (28 to 101µm)Width: .2” to 80” (50.8 to 2032mm)Core size: 3” and 6” standard cores, 8” availableRoll O.D.: various confiations availableCustom colors and ti..
Tensile Modulus	2.76 GPa	400 ksi	ASTM D638
Quantum PET Information provided by Quantum Advanced Engineering Plastics
Tensile Modulus	2.76 GPa	400 ksi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Stat-Tech™ AS-10CP/000 Acrylonitrile Butadiene Styrene (ABS) (discontinued **) Description/Features:AntistaticConductive Carbon Powder FilledInformation provided by PolyOne Corporation.
Tensile Modulus	2.76 GPa	400 ksi	ASTM D638
Spartech Polycast MP 1.25 (UL 752 Level 1) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech.
Tensile Modulus	2.76 GPa	400 ksi
Master Bond EP30P Epoxy Bonds Glass, Polycarbonates and Acrylics Description: Master Bond Polymer Adhesive EP30P is a two component, transparent, low viscosity epoxy resin system for high performance bonding, sealing, coating, encapsulating and casting. It is for..
Tensile Modulus	2.76 GPa	400 ksi
Master Bond EP33CLV Epoxy Resists Chemicals and High Temperatures Description: Master Bond EP33CLV is a two part, room temperature curing epoxy system used for bonding, sealing and coating featuring high temperature resistance, good dimensional stability and excel..
Tensile Modulus	2.76 GPa	400 ksi	ASTM D638
Ensinger Tecamid® GF30 Extruded Nylon 6/6 30% glass-fiber-reinforced (PA66) Tecamid® 6/6 GF30 is a 30% glass-fiber reinforced nylon 6/6 material whose important properties include high tensile and flexural strength, stiffness, excellent heat deflection temperature, and sup..
Tensile Modulus	2.76 GPa	400 ksi	ASTM D-638
Axiall 9275J Clear 40 Rigid PVC, Molding, Clear 40 Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Modulus	2.76 GPa	400 ksi	ASTM D-638
Axiall 8240 Rigid PVC, Extrusion Georgia Gulf 8240 is a general-purpose rigid PVC extrusion compound designed for applications requiring the following properties: Rigidity/StiffnessGlossImpact Strength & ToughnessFlame RetardantCh..
Tensile Modulus	2.76 GPa	400 ksi	TM R050-36
Resinlab® EP1296 Highly Filled, Moderately Thixotropic Black Casting Resin Resinlab™ EP1296 is a highly filled, moderately thixotropic black casting resin designed for applications requiring good thermal conductivity, low shrinkage and a low CTE. It was especially formula..
Tensile Modulus	2.76 GPa	400 ksi	TM R050-36
Resinlab® EP691 Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP691 is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has good wetting and ad..
Tensile Modulus	2.76 GPa	400 ksi	ASTM D-638
Axiall 6511 Rigid PVC, Molding Georgia Gulf 6511 is a special purpose rigid PVC compound designed for applications requiring the following properties: GlossImpact Strength & ToughnessFlame RetardantChemical ResistantThermoformab..
Tensile Modulus	2.76 GPa	400 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ ATH-000/10T 2S Acetal (POM) Homopolymer (discontinued **) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..