PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer PolyOne Corporation
Trade Name Maxxam™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.998 g/cc
0.998 g/cc
ASTM D792
Melt Flow 2.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 15.9 MPa
2310 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 500 %
500 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 1.10 GPa
160 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 17.2 MPa
2490 psi
ASTM D790
Flexural Modulus 0.510 GPa
74.0 ksi
ASTM D790
Izod Impact, Notched 0.690 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.29 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Gardner Impact 15.8 J

@Thickness 3.18 mm,
Temperature 23.0 °C
11.7 ft-lb

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 54.0 °C

@Thickness 3.18 mm
129 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 46.0 °C

@Thickness 3.18 mm
115 °F

@Thickness 0.125 in
Annealed; ASTM D648
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
ALL; UL 94
V-0

@Thickness 6.00 mm
V-0

@Thickness 0.236 in
NC; UL 94
Oxygen Index 26 %

@Thickness 3.18 mm
26 %

@Thickness 0.125 in
ASTM D2863
Descriptive Properties Value Comments
Features Flame Retardant
Forms Pellets
Generic Material PE, Unspecified
Generic Name Polyethylene, Unspecified (PE, Unspecified)
Processing Method Rotational Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
South America