- Polymer Property : Tensile Strength, Yield = 15.9 MPa
Polymer Property : Tensile Strength, Yield = 15.9 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Syncure™ System S112BL Polyethylene, Crosslinked (XLPE) Syncure™ systems are two part moisture crosslinkable compounds. S112BL is a CSA listed, high strength, weather resistant, black (2.5% carbon black) cable insulation compound. RoHS compliant.STORAGE.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | ASTM D638 |
| ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good flowUses: Consumer items, Potable water tanks, Laundry tubs |
|||
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 22% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | Elastic; ASTM D412 |
| Multibase Multi-Flex® D 4701 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good I.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | Elastic; ASTM D412 |
| Multibase Multi-Flex® D 3104 TPO Thermoplastic Polyolefin Elastomer Features: Chemical Resistance, Good PaintableOzone Resistant Thermal Stability, GoodDensity, LowTear Strength, Good Forms:PelletsProcessing Method:Injection Molding Uses: Automotive ApplicationsI.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | Longitudinal |
| Saint-Gobain Norton® Fluorglas® Chemfilm® R128/R129 Premium Grade Extruded Full Density PTFE Film (0.003" thick) Description: Full Density Unsintered Tape is used as primary insulation for high-temperature wires, jackets and cables and wall for convoluted hose. It meets the requirements of component insulation.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-412-98 |
| Saint-Gobain Vendflow® E-70-V-CE Taste Barrier Tubing Formulation Description: Non-plasticized inner bore yeilds no taste: Vendflow® E-70-V-CE is specifically formulated to transfer water and beverages without imparting any "plastic" taste sometimes found in PV.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | |
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 80 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | at 200%; ASTM D412 |
| Lubrizol Estane® ALR PC60D Thermoplastic Polyurethane Type: Estane® ALR PC60D is a polycarbonate diol based thermoplastic polyurethane (TPU).Features: Hydrolytically stable, very durableInformation Provided by The Lubrizol Corporation |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | At 20 in/min; ASTM D638 |
| Borealis SuperTR™ LE4212 Scorch Retardant, Crosslinkable Polyethylene, Water Tree Retardant Insulation for Me Power Cables SuperTR LE4212 is a natural, crosslinkable low density polyethylene compound, which has water tree retardant and scorch retardant properties.SuperTR LE4212 has been specifically developed as a scorc.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall EX1264 Moldings & Extrusions Flexible PVC General purpose extrusion compound designed for water stop applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0437C30L1 Calcium Reinforced |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 13821 Wire & Cable Flexible PVC Non-lead stabilized, 720 hour sunlight resistant, TW insulation compound also recommended for 75C Class 43 applications or outdoor jacket applications.Information provided by Georgia GulfGeorgia Gul.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 190 Moldings & Extrusions Flexible PVC 60C plug molding component. UL recognized component for 94 V-0 in all colors. 1.13 mm minimum thickness. UL QMFZ2 recognized component.Information provided by Georgia GulfGeorgia Gulf became Axia.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 2110 Wire & Cable Flexible PVC Tray cable jacket for 105°C applications. Also suitable for direct burial applications. UL recognized for 720 hour sunlight resistance in all colors.Information provided by Georgia GulfGeorgia Gu.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 37740 Wire & Cable Flexible PVC 90°C rated compound designed for use as an inner and outer jacket in Teck 90 cables.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 898 Wire & Cable Flexible PVC Non-lead stabilized, flame retardant, non-migratory, 105°C insulation compound recommended for use in non-migratory applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corpo.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 19850 Moldings & Extrusions Flexible PVC Primary insulation compound recommended for 105C, 1/32 wall and larger applications. Also well suited for plug molding. UL rated 94 HB.Information provided by Georgia GulfGeorgia Gulf became Axial.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | 2"/min; ASTM D638 |
| A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
| Tensile Strength, Yield | 15.9 - 44.5 MPa | 2310 - 6450 psi | Average value: 28.5 MPa Grade Count:92 |
| Overview of materials for Cellulose Acetate Butyrate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 22% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D-638 |
| Axiall 8863 Moldings & Extrusions Flexible PVC A vinyl elastomer extrusion compound with rubber-like properties. Ideally suited for extruded profiles and tubings. Meets the requirements for LP Gas hose per UL21.Information provided by Georgia .. |
|||
| Tensile Strength, Yield | 15.9 MPa | 2300 psi | ASTM D638 |
| Multibase Multi-Flam™ 0107 HDPE Polyethylene Features:Flame RetardantHalogen Content, Low to None Forms:PelletsProcessing Methods:Injection MoldingCoextrusionExtrusionUses:TubingPipingInformation provided by Multibase |
|||