PolyOne Versalloy™ XL 9070X-9 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versalloy™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versalloy™ XL 9070X-9 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versalloy™ XL 9070X-9 is a TPV alloy with exceptional flow properties and surface aesthetics for a variety of applications. - Exceptional Flow for Long, Thin Flow Paths - Overmold Adhesion to Polypropylene - Superior Surface Aesthetics - Very Good Mar ResistanceVersalloy™ XL 9070X-9 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times. Municipality waste stream recycle code is 7 which is designated for Other. Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versalloy™ XL 9070X-9 with minimal property losses, provided that the regrind is free of contamination. To mimimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Drying is not Required Injection Speed: 1 to 5 in/sec 1st Stage - Boost Pressure: 300 to 700 psi 2nd Stage - Hold Pressure: 70% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.888 g/cc
0.888 g/cc
ASTM D792
Viscosity 6200 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
6200 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Linear Mold Shrinkage, Flow 0.014 - 0.020 cm/cm
0.014 - 0.020 in/in
ASTM D955
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
280 g/10 min

@Load 5.00 kg,
Temperature 200 °C
280 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 69
69
10 sec; ASTM D2240
Tensile Strength at Break 5.43 MPa

@Temperature 23.0 °C
788 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 2.48 MPa

@Strain 100 %,
Temperature 23.0 °C
360 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
3.53 MPa

@Strain 300 %,
Temperature 23.0 °C
512 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 580 %

@Temperature 23.0 °C
580 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 31.5 kN/m
180 pli
ASTM D624
Compression Set 23 %

@Temperature 23.0 °C,
Time 79200 sec
23 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
42 %

@Temperature 70.0 °C,
Time 79200 sec
42 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395B
53 %

@Temperature 100 °C,
Time 79200 sec
53 %

@Temperature 212 °F,
Time 22.0 hour
ASTM D395B
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 149 - 188 °C
300 - 370 °F
Middle Barrel Temperature 160 - 199 °C
320 - 390 °F
Front Barrel Temperature 171 - 210 °C
340 - 410 °F
Nozzle Temperature 171 - 210 °C
340 - 410 °F
Mold Temperature 15.6 - 26.7 °C
60.1 - 80.1 °F
Back Pressure 0.689 - 1.38 MPa
99.9 - 200 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Agency Ratings FDA 21 CFR 177.1210
Please contact GLS Thermoplastic Elastomers for a copy of the FDA compliance letter.
UL 94 .QMFZ2.E76261
Appearance Black
Features Good Flow
Good Surface Finish
Recyclable Material
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Consumer Applications
Overmolding
Soft Touch Applications
Thin-walled Parts