Polymer Resources NY66-IM2-LM Nylon, Preliminary Data Sheet, Low Flexural Modulus, High Impact (DAM)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-IM2-LM Nylon, Preliminary Data Sheet, Low Flexural Modulus, High Impact (DAM).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Linear Mold Shrinkage 0.017 - 0.020 cm/cm
0.017 - 0.020 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.4 MPa
6000 psi
ASTM D638
Tensile Strength, Yield 41.4 MPa
6000 psi
ASTM D638
Flexural Strength 51.7 MPa
7500 psi
ASTM D790
Flexural Modulus 1.36 GPa
197 ksi
ASTM D790
Izod Impact, Notched 9.08 J/cm
17.0 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 202 °C
395 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 57.2 °C
135 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 266 - 277 °C
510 - 530 °F
Middle Barrel Temperature 271 - 282 °C
520 - 540 °F
Front Barrel Temperature 277 - 288 °C
530 - 550 °F
Melt Temperature 277 - 293 °C
530 - 560 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3 - 4 hour
3 - 4 hour