Polymer Resources NY66-IMG33 Nylon, 33% Glass Reinforced, Impact Modified (DAM)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY66-IMG33 Nylon, 33% Glass Reinforced, Impact Modified (DAM).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
ASTM D638
Tensile Strength, Yield 138 MPa
20000 psi
ASTM D638
Flexural Strength 214 MPa
31000 psi
ASTM D790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm
2.50 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 243 °C
470 °F
ASTM D648
Flammability, UL94 HB
HB
1/16 in
Processing Properties Metric English Comments
Rear Barrel Temperature 293 - 304 °C
560 - 580 °F
Middle Barrel Temperature 277 - 288 °C
530 - 550 °F
Front Barrel Temperature 271 - 282 °C
520 - 540 °F
Melt Temperature 288 - 299 °C
550 - 570 °F
Mold Temperature 65.6 - 104 °C
150 - 220 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3 - 4 hour
3 - 4 hour