Polymer Resources PPX/NY G10 Modified PPO, 10% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX/NY G10 Modified PPO, 10% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.010 cm/cm
0.0050 - 0.010 in/in
ASTM D955
Melt Flow 2.0 - 8.0 g/10 min
2.0 - 8.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.2 MPa
12500 psi
ASTM D638
Tensile Strength, Yield 86.2 MPa
12500 psi
ASTM D638
Flexural Strength 141 MPa
20500 psi
ASTM D790
Flexural Modulus 3.52 GPa
510 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm
0.900 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 204 °C
400 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 216 °C
420 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 268 - 302 °C
515 - 575 °F
Middle Barrel Temperature 274 - 302 °C
525 - 575 °F
Front Barrel Temperature 279 - 302 °C
535 - 575 °F
Melt Temperature 279 - 302 °C
535 - 575 °F
Mold Temperature 79.4 - 121 °C
175 - 250 °F
Drying Temperature 93.3 - 107 °C
200 - 225 °F
Dry Time 3 - 5 hour
3 - 5 hour