Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler
Manufacturer Polyram
Trade Name Polytron
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A chemically coupled 50% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ASTM-D792
Linear Mold Shrinkage 0.00030 cm/cm
0.00030 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 135 MPa
19600 psi
ASTM-D638
Elongation at Break 2.0 %
2.0 %
ASTM-D638
Tensile Modulus 13.3 GPa
1930 ksi
ASTM-D790
Flexural Strength 210 MPa
30500 psi
ASTM-D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM-D790
Izod Impact, Notched 2.50 J/cm

@Temperature 23.0 °C
4.68 ft-lb/in

@Temperature 73.4 °F
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 159 °C
318 °F
ASTM-D648
Processing Properties Metric English Comments
Rear Barrel Temperature 210 °C
410 °F
Middle Barrel Temperature 215 °C
419 °F
Front Barrel Temperature 220 °C
428 °F
Nozzle Temperature 215 °C
419 °F
Melt Temperature 220 °C
428 °F
Mold Temperature 65.0 °C
149 °F
Injection Velocity 50.0 mm/sec
1.97 in/sec
Back Pressure 0.150 - 0.350 MPa
21.8 - 50.8 psi
Cushion 0.650 cm
0.256 in
Screw Speed 50 rpm
50 rpm