- Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber Filled
- SABIC Innovative Plastics LNP Faradex AS0029 ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Faradex AS0029 ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP FARADEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Faradex AS0029 ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Faradex* AS-1002 FR is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: Flame Retardant, EMI/RFI Shielding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
36.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 2.50 mm |
V-0 @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- NanoAmor 90% Regular Single Walled Carbon Nanotubes
- Polymer Resources NY66-M40-[color]-H Nylon 66, 40% Mineral Filled, Heat Stabilized
- Chevron Phillips MarFlex® ER3343 Polyethylene; Masterbatch (discontinued **)
- HP Alloys Alloy 718, 15% Cold Worked, Aged
- Chase Plastics CP Pryme® N110L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated
- Total HDPE XLS 12 B High Density Polyethylene - Pipes and Fittings
- Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding
- Colorite Polymers 9273E General Purpose Vinyl Compound
- EMS-Grivory Grivory® GV-6H PA*-GF60
- CeramTec Rubalit® 708 HP Alumina, 96% (High Performance)
Copyright © lookpolymers.com All Rights Reserved