SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP * Lubricomp * HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.026 cm/cm
0.026 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.0 MPa
5950 psi
50 mm/min; ISO 527
Tensile Strength, Yield 41.0 MPa
5950 psi
50 mm/min; ISO 527
Elongation at Break 225 %
225 %
50 mm/min; ISO 527
Elongation at Yield 115 %
115 %
50 mm/min; ISO 527
Tensile Modulus 1.20 GPa
174 ksi
1 mm/min; ISO 527
Flexural Yield Strength 12.0 MPa
1740 psi
2 mm/min; ISO 178
Flexural Modulus 0.300 GPa
43.5 ksi
2 mm/min; ISO 178
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 210 µm/m-°C

@Temperature 23.0 - 60.0 °C
 117 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 190 µm/m-°C

@Temperature 23.0 - 60.0 °C
 106 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af