SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* OEP32 is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| 127 MPa | 18400 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 10.56 GPa | 1532 ksi | 50 mm/min; ASTM D638 |
| 10.59 GPa | 1536 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 431 MPa | 62500 psi | ISO 178 | |
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.28 J/cm | 8.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 78.6 x 10-8 mm³/N-M | 39.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ U 5365A-E0134 FG Thermoplastic Elastomer (TPE)
- Ritelok TL42 Nutlock
- PolyOne Stat-Tech™ PI-05CF/000 Polyetherimide - 5% Carbon Fibers - ESD Applications (discontinued **)
- ExxonMobil SAE 30 Mobilgard ADL Series
- Eagle Brass 762 Nickel Silver 12%, Hard
- DSM Akulon® F136-C1 PA6
- EMS-Griltech Griltex® D 1357E Copolyester Hotmelt Adhesive (Apparel Interlinings)
- Chicago Extruded Metals UNS C48500 Copper-Zinc-Tin Alloy
- Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Conditioned, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved