SABIC Innovative Plastics Valox® V8280SF PBT+PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V8280SF PBT+PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 265 °C |
45 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Melt Index of Compound | 30 g/10 min @Load 2.16 kg, Temperature 265 °C |
30 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 135 MPa | 19600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 135 MPa | 19600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 90 % | 90 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 |
| 13.5 GPa | 1960 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 190 MPa | 27600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.0 GPa | 1740 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 920ASR PC
- Sumitomo Bakelite Durez® 31906 Phenolic, Injection Grade
- Unipetrol SH Sorbent Chezacarb
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.25 PHR Zinc Stearate
- Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control
- DuPont™ Kapton® 300HN Polyimide Film, 75 Micron Thickness
- EMS-Grivory Grivory® LKN-5H PA12-GB50
- Eurostar Staramide BG6U PA6, 30% Glass Fiber Filled, UV Stabilized, Injection Molded
- BASF Ultraform® N2520 XL2 POM
- RheTech Products HP510-01UV 28% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved