Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBRE™ MEGARAD™ 2091 Polycarbonate Resins are designed for single use medical devices (SUDs) that require gamma and electron-beam irradiation and an accelerated schedule for delivery of post-radiated products to customers – potentially 10 to 21 days sooner than currently available radiation-stabilized polycarbonate resins, depending on irradiation conditions. In addition, the resins are meant for applications that require a more water white appearance rather than the traditional purple tinted resin used to compensate for these sterilization methods. CALIBRE™ MEGARAD™ 2091-15 Polycarbonate resins has undergone biocompatibility texting based on ISO 10993 standards (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics:ISO 10993 (in progress)Mold ReleaseImproved Color CompensationApplications:Medical ApplicationsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/B; ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527-2/50 |
| 68.3 MPa | 9910 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ISO 527-2/50 |
| 62.1 MPa | 9010 psi | 50 mm/min; ASTM D638 | |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| 98.0 MPa | 14200 psi | 3-point, 2.0 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.50 J/cm @Temperature 23.0 °C |
14.1 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256; ISO 180 |
| Tensile Impact Strength | 378 kJ/m² | 180 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 81.3 J | 60.0 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1044 |