Styron CALIBREâ„¢ IM 401-11 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ IM 401-11 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ IM 401-11 Impact Modified Polycarbonate resin is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy process with improved impact strength in highly filled formulations Main Characteristics:Impact modifiedSuperior low temperature toughnessApplications:Automotive interiorsAutomotive exteriorsSmall & large applicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183/B; ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ISO 294-4; ASTM D955
Melt Flow 11 g/10 min

@Load 1.20 kg,
Temperature 300 °C
11 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.8 MPa
8090 psi
50 mm/min; ASTM D638
56.0 MPa
8120 psi
ISO 527-2/50
Elongation at Break 130 %
130 %
50 mm/min; ASTM D638; ISO 527-2/50
Flexural Strength 89.6 MPa
13000 psi
Method I (3 point load), 2.0 mm/min; ASTM D790
90.0 MPa
13100 psi
2.0 mm/min, 3 point; ISO 178
Flexural Modulus 2.27 GPa
329 ksi
2.0 mm/min, 3 point; ISO 178
2.28 GPa
331 ksi
Method I (3 point load), 2.0 mm/min; ASTM D790
Izod Impact, Notched 6.90 J/cm

@Temperature 23.0 °C
12.9 ft-lb/in

@Temperature 73.4 °F
ASTM D256; ISO 180/4A
Tensile Impact Strength 630 kJ/m²
300 ft-lb/in²
ASTM D1822
Dart Drop, Total Energy 56.5 J
41.7 ft-lb
3.39 m/sec; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed; ASTM D648; ISO 75-2/B
136 °C
277 °F
Annealed; ASTM D648; ISO 75-2/B
Vicat Softening Point 145 °C

@Load 5.10 kg
293 °F

@Load 11.2 lb
Rate A (50°C/h); ASTM D1525; ISO 360/B50
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in