Styron EMERGEâ„¢ 4310-15 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 4310-15 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMERGEâ„¢ PC 4310-15 advanced resin is high-performance polycarbonate resin offering high heat resistance and maximum toughness. Applications: Consumer Electronics and Information Technology Equipment Computer and Business Equipment Portable Electronics Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength, Ultimate 71.0 MPa
10300 psi
0.125 in, injection molded, unannealed; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
0.125 in, injection molded, unannealed; ASTM D638
Elongation at Break 150 %
150 %
0.125 in, injection molded, unannealed; ASTM D638
Tensile Modulus 2.34 GPa
340 ksi
0.125 in, injection molded, unannealed; ASTM D638
Flexural Strength 96.5 MPa
14000 psi
0.125 in, injection molded, unannealed; ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
0.125 in, injection molded, unannealed; ASTM D790
Izod Impact, Notched 8.54 J/cm
16.0 ft-lb/in
ASTM D256
Dart Drop, Total Energy 87.0 J
64.2 ft-lb
8000 ipm; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 68.4 µm/m-°C

@Temperature -40.0 - 82.2 °C
38.0 µin/in-°F

@Temperature -40.0 - 180 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
289 °F
0.157 in, annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
0.157 in, unannealed; ASTM D648
140 °C
284 °F
0.157 in, annealed; ASTM D648
Vicat Softening Point 148 °C
298 °F
50°C/hr, 50N; ASTM D1525
Flammability, UL94 HB
HB
0.0630 in
HB
HB
0.120 in
Oxygen Index 26 %
26 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 60 Hz
3.0

@Frequency 60 Hz
ASTM D150
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 16.5 kV/mm
420 kV/in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60 Hz
0.0010

@Frequency 60 Hz
ASTM D150
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
ASTM D150