Supreme Petrochem SP 6503 High Impact Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Supreme Petrochem LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Supreme Petrochem SP 6503 High Impact Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics High Impact Available in various colors Easy flow High stiffness Processing Injection moldingApplications Computer cabinet, printer body, business machine housing etc. Material Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Melt Flow 4.2 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 4.2 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
48 g/10 min

@Load 10.0 kg,
Temperature 200 °C
 48 g/10 min

@Load 22.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.9 MPa
4630 psi
50 mm/min; ASTM D638
Elongation at Break 40 %
40 %
50 mm/min; ASTM D638
Flexural Strength 51.4 MPa

@Thickness 3.20 mm
 7450 psi

@Thickness 0.126 in
 ASTM D790
Flexural Modulus 1.96 GPa

@Thickness 3.20 mm
 284 ksi

@Thickness 0.126 in
 ASTM D790
Izod Impact, Notched 1.25 J/cm

@Thickness 3.20 mm
 2.34 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
ASTM D648
Vicat Softening Point 105 °C
221 °F
1kg / 120°C; ASTM D1525
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 180 - 260 °C
356 - 500 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F