TSE Industries EcoWIND® M110 General Purpose Filament Winding Polyurethane Resin

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Liquid
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries EcoWIND® M110 General Purpose Filament Winding Polyurethane Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® resins are formulated for filament winding applications serving the composite pressure vessel, tank, and piping markets. These PU resins have tested positively in both hot and cold pressure vessel applications and can be applied to reinforce thermoplastic substrates (i.e. polyethylene, ABS, etc.) or applied directly to a release coated mandrel surface.All information provided by TSE Industries
Physical Properties Metric English Comments
Viscosity 100 - 400 cP

@Temperature 45.0 °C
100 - 400 cP

@Temperature 113 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.0 MPa
9570 psi
Plain Cast Resin; ASTM D638
Elongation at Break 3.5 - 4.5 %
3.5 - 4.5 %
Plain Cast Resin; ASTM D638
Modulus of Elasticity 3.20 GPa
464 ksi
Plain Cast Resin; ASTM D638
Flexural Yield Strength 97.5 MPa
14100 psi
Plain Cast Resin; ASTM D790
Flexural Modulus 2.70 GPa
392 ksi
Plain Cast Resin; ASTM D790
Izod Impact, Notched 4.30 J/cm
8.06 ft-lb/in
Plain Cast Resin; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C
129 °F
Plain Cast Resin; ASTM D648
Glass Transition Temp, Tg 83.0 °C
181 °F
Plain Cast Resin; ASTM D3418
Processing Properties Metric English Comments
Pot Life 15.0 - 20.0 min

@Temperature 23.0 °C
15.0 - 20.0 min

@Temperature 73.4 °F