Teijin Panlite® G-3310M Isotropic, Glass Fiber Reinforced Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® G-3310M Isotropic, Glass Fiber Reinforced Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Reinforced with 10 % of special GF and least anisotropy grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPrecision machinery components that need dimensional accuracy, particularly least anisotropyComponents that need paint finish.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Water Absorption 0.16 %
0.16 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50mm/min; ISO 527
Elongation at Break 60 %
60 %
50mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
2mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
255 °F
ISO 75
Vicat Softening Point 140 °C
284 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 130 °C

@Thickness 1.47 mm
266 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 120 °C

@Thickness 1.47 mm
248 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 1.47 mm
266 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
IEC 60250
3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112