Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Homopolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Tisan Engineering Plastics
Trade Name TISOPLEN®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Homopolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow moisture intakeHigh impact resistanceExcellent chemical resistanceElectrical isolationHigh performance/affordable priceEasy processability Mineral filled TISOPLEN compounds have a long lasting thermal-dimensional stability, increased mechanical and hardness characteristics, decreased mold shrinkage and improved surface appearance. Glass fiber reinforcement will impart high tensile strength and impact resistance and yield improvements in thermal characteristics of TISOPLEN products. Excellent resistance to weak acids, weak alkalis, and strong alkalis. Good resistance to strong acids and alcohols. Medium resistance to hydrocarbons and engine fuels. Weak resistance to organic solvents.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
Melt Flow 13 g/10 min
13 g/10 min
ISO 1133
Ash 20 %
20 %
ISO 3451
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
ISO 527-2
Tensile Strength, Yield 32.0 MPa
4640 psi
ISO 527-2
Elongation at Break 26 %
26 %
ISO 527-2
Elongation at Yield 27 %
27 %
ISO 527-2
Modulus of Elasticity 2.35 GPa
341 ksi
ISO 527-2
Izod Impact, Notched (ISO) 4.50 kJ/m²
2.14 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
Vicat Softening Point 125 °C
257 °F
ISO 306
Heat Distortion Temperature 130 °C
266 °F
ISO 75-2
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 70.0 °C
158 °F
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Aft-1. Region Temperature
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Mid-2. Region Temperature
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Pre-3. Region Temperature
Nozzle Temperature 200 °C
392 °F
Melt Temperature 170 - 190 °C
338 - 374 °F
Drying Temperature 80.0 °C
176 °F
Predrying Temperature
Dry Time 1 hour
1 hour
Predrying Time
Moisture Content 0.010 %
0.010 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 45°C
Copyright © lookpolymers.com All Rights Reserved