Tisan TISOPLEN® 30% Glass Fiber Filled Reinforced Heat Stabilized Homopolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Tisan Engineering Plastics
Trade Name TISOPLEN®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISOPLEN® 30% Glass Fiber Filled Reinforced Heat Stabilized Homopolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow moisture intakeHigh impact resistanceExcellent chemical resistanceElectrical isolationHigh performance/affordable priceEasy processability Mineral filled TISOPLEN compounds have a long lasting thermal-dimensional stability, increased mechanical and hardness characteristics, decreased mold shrinkage and improved surface appearance. Glass fiber reinforcement will impart high tensile strength and impact resistance and yield improvements in thermal characteristics of TISOPLEN products. Excellent resistance to weak acids, weak alkalis, and strong alkalis. Good resistance to strong acids and alcohols. Medium resistance to hydrocarbons and engine fuels. Weak resistance to organic solvents.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
Ash 30 %
30 %
ISO 3451
Mechanical Properties Metric English Comments
Hardness, Shore A 69
69
ISO 868
Tensile Strength at Break 95.0 MPa
13800 psi
ISO 527-2
Tensile Strength, Yield 94.0 MPa
13600 psi
ISO 527-2
Elongation at Break 3.0 %
3.0 %
ISO 527-2
Elongation at Yield 3.0 %
3.0 %
ISO 527-2
Modulus of Elasticity 5.80 GPa
841 ksi
ISO 527-2
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
Vicat Softening Point 140 °C
284 °F
ISO 306
Heat Distortion Temperature 160 °C
320 °F
ISO 75-2
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 70.0 °C
158 °F
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Aft-1. Region Temperature
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Mid-2. Region Temperature
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Pre-3. Region Temperature
Nozzle Temperature 200 °C
392 °F
Melt Temperature 170 - 190 °C
338 - 374 °F
Drying Temperature 80.0 °C
176 °F
Predrying Temperature
Dry Time 1 hour
1 hour
Predrying Time
Moisture Content 0.010 %
0.010 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 45°C
Copyright © lookpolymers.com All Rights Reserved