Total Lotrene® Q1018N Linear Low Density Polyethylene, Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer Total Atofina
Trade Name Lotrene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lotrene® Q1018N Linear Low Density Polyethylene, Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lotrene® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion of co-extrusion process to modify film properties. This grade contains thermal stabilizers.Lotrene® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films...Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.918 g/cc
0.918 g/cc
ASTM D792
Thickness 40.0 microns
1.57 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 0.000 ppm
0.000 ppm
Slip Level 0.000 ppm
0.000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 800 %
800 %
ASTM D882
Film Elongation at Break, TD 850 %
850 %
ASTM D882
Elmendorf Tear Strength, MD 7.10 g/micron
180 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 12.2 g/micron
310 g/mil
ASTM D1922
Dart Drop Test 150 g
0.331 lb
F50; ASTM D1709
Film Tensile Strength at Break, MD 38.0 MPa
5510 psi
ASTM D882
Film Tensile Strength at Break, TD 33.0 MPa
4790 psi
ASTM D882
1% Secant Modulus, MD 215 MPa
31200 psi
ASTM D882
1% Secant Modulus, TD 245 MPa
35500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 122 °C
252 °F
Crystalline; ISO 11357
Vicat Softening Point 100 °C
212 °F
ASTM D1525 (A120)
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D1003
Gloss 60 %
60 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 220 °C
356 - 428 °F
Extrusion
Melt Temperature 200 °C
392 °F
Die Opening >= 0.180 cm
>= 0.0709 in
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0