Tra-Con Tra-Bond F113 High Impact Optically Clear Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond F113 High Impact Optically Clear Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND F113 is an optically clear, low viscosity, high impact epoxy adhesive developed for bonding and small volume potting of plastic or glass optical fibers, lenses, and prisms, LED displays, and other optical components. It is recommended for laminating, bonding, and sealing applications where excellent wetting, good pot life and improved impact strength properties are required. This two part adhesive is easily mixed and cured at room temperature, and develops strong, tough bonds to glass and glass fibers, ceramics, many metals, and most rigid plastics. TRA-BOND F113 bonds offer resistance to mechanical impact and thermal shock, and are also resistant to weather, water, gases and vapors, petroleum products, salts, and mild acids and alkalis.Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
Mixed
Viscosity 180 cP

@Temperature 25.0 °C
180 cP

@Temperature 77.0 °F
After mixing
Mechanical Properties Metric English Comments
Hardness, Shore D 78
78
Adhesive Bond Strength 27.6 MPa
4000 psi
Lap shear, alum to alum, 2 hrs @ 65°C
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C

@Temperature 20.0 °C
30.6 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 100 °C
212 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Glass Transition Temp, Tg 45.0 °C
113 °F
Ultimate Tg
Optical Properties Metric English Comments
Refractive Index 1.55
1.55
Transmission, Visible 97 %
97 %
3200-9000 Å
Electrical Properties Metric English Comments
Volume Resistivity 9.00e+8 ohm-cm
9.00e+8 ohm-cm
Dielectric Constant 4.8

@Frequency 1000 Hz
4.8

@Frequency 1000 Hz
Dielectric Strength 16.9 kV/mm
430 kV/in
Processing Properties Metric English Comments
Cure Time 60.0 - 120 min

@Temperature 65.0 °C
1.00 - 2.00 hour

@Temperature 149 °F
1440 min

@Temperature 25.0 °C
24.0 hour

@Temperature 77.0 °F
Pot Life 120 min
120 min
Descriptive Properties Value Comments
Color Transparent, Clear
Mix Ratio, parts by weight 100/30
Resin/Hardener
Thixotropic Index 1
Working Life hours 3