Arkema Group Pebax® 2533 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 2533 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr in water at 20°C; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | 20°C and 65% RH; ASTM D570 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | ASTM D2240 |
| Hardness, Shore D | 25 | 25 | ASTM D2240 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 790 % | 790 % | ASTM D638 |
| Modulus of Elasticity | 0.0104 GPa | 1.51 ksi | ASTM D638 |
| Flexural Modulus | 0.0150 GPa | 2.18 ksi | ASTM D790 |
| Resilience | 0.75 | 0.75 | BS 903 par: A 8 |
| Flex Crack Resistance | 2.0 | 2.0 | [mm] 20°C / 100000 flexures; ASTM D813 |
| 2.5 | 2.5 | [mm] -20°C / 50000 flexures; ASTM D813 | |
| Izod Impact, Notched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Izod Impact, Unnotched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Tear Strength | 38.0 kN/m | 217 pli | notched; ASTM D624 (C) |
| 58.0 kN/m | 331 pli | unnotched; ASTM D624 (C) | |
| Taber Abrasion, mg/1000 Cycles | 94 | 94 | ASTM D1242 |
| Abrasion | 155 | 155 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 62 % | 62 % | Load = 9.3 MPa (22 hr / 70°C); ASTM D395 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 5.00 J/g | 2.15 BTU/lb | ASTM D3417 |
| CTE, linear | 200 µm/m-°C @Temperature -40.0 - 140 °C |
111 µin/in-°F @Temperature -40.0 - 284 °F |
ASTM D696 |
| Melting Point | 133.5 °C | 272.3 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
| Vicat Softening Point | 60.0 °C | 140 °F | under 1 daN; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.00e+12 ohm @Temperature 20.0 °C |
3.00e+12 ohm @Temperature 68.0 °F |
65% RH; ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 FRC 2 PA66, basic type
- SABIC Innovative Plastics LNP Faradex NS0039 PC/ABS (Europe-Africa-Middle East)
- Parker Chomerics CHO-SEAL® 6307 Conductive Elastomer
- SABIC Innovative Plastics Lexan® HPH4704 PPC (Europe-Africa-Middle East)
- SCG Chemicals EL-Proâ„¢ P401S Polypropylene Flat Yarn/Sheet
- Master Bond EP13 High Temperature Resistant One Component Epoxy System
- Borealis HF700SA Polypropylene
- EPICHEM Epinyl PA 6 GF 30 ATP Polyamide 6, 30% Glass
- ExxonMobil 13M Mobil DTE 10M Series
- Arlon R31246R063 0.063" (1.60 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved