Arkema Group Rilsan® AZM 50 NOIR T6LD Nylon 12, 50% Glass Fiber Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 50% Glass Fiber Filled
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AZM 50 NOIR T6LD Nylon 12, 50% Glass Fiber Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,MHLR,16-090,GF50Rigid grade with glass fiber (50%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigidity. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Mechanical parts with very high rigidity.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Melt Flow 1.1 g/10 min

@Load 2.16 kg,
Temperature 235 °C
1.1 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 145 MPa
21000 psi
5 mm/min
Elongation at Break 4.0 %
4.0 %
5 mm/min
Tensile Modulus 14.8 GPa
2150 ksi
1 mm/min
Charpy Impact Unnotched 8.58 J/cm²
40.8 ft-lb/in²
9.29 J/cm²

@Temperature -30.0 °C
44.2 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 2.29 J/cm²
10.9 ft-lb/in²
1.72 J/cm²

@Temperature -30.0 °C
8.19 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Surface Resistance 1.00e+11 ohm
1.00e+11 ohm