Arlon R39118R037L 0.037" (0.940 mm) Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R39118R037L 0.037" (0.940 mm) Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Design/Construction: Interleave: Polyester Release Liner Transfer Pressure Sensitive Adhesive: Silicone PSASide 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Cured Silicone RubberProduct Use: Masking TapeAppearance: Red silicone rubber tape with pressure sensitive adhesive on one sideThis data represents typical values for the production material. The data should not be used to write, or in place of, material specificationsInformation provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	50.8 microns	2.00 mil	Transfer PSA; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Side 1 add-on thickness; Arlon SQA-TMS-003
	102 microns	4.00 mil	Interleave
	203 microns	8.00 mil	Substrate; Arlon SQA-TMS-003
	610 microns	24.0 mil	Side 2 add-on thickness; Arlon SQA-TMS-003
	940 microns	37.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55	55	Silicone Property; ASTM D2240
Tensile Strength	9.65 MPa	1400 psi	Silicone Property; ASTM D412
Elongation at Break	500 %	500 %	Silicone Property; ASTM D412
Peel Strength	0.614 kN/m	3.50 pli	Bond Strength (psa to SS); Arlon SQA-TMS-011
	0.701 kN/m	4.00 pli	Bond Strength (psa to psa); Arlon SQA-TMS-011

Processing Properties	Metric	English	Comments
Shelf Life	12.0 Month @Temperature 21.1 °C	12.0 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	33.6	Arlon SQA-TMS-025